Titanium anode baskets

Titanium anode baskets is available for Plating factory and PCB factory for electroplating - details see: https://www.machineto.com/titanium-anode-baskets-10281630

Place of Origin:GUA,Guangdong, China (Mainland) China (Mainland)

Brand Name:BAODA

Titanium anode baskets:

Titanium Anode Baskets
Material	unalloyed/pure titanium
Grade	Gr1,Gr2
Technology Standard	ASTM B265
Specification	Length x Width x Thickness 400x120x50mm,500x130x55mm,600x150x55mm, 700x175x60mm, 800x195x60mm,900x215x65mm, 1000x250x65mm,400x120x50mm,500x130x55mm, 600x150x55mm,700x175x60mm,800x195x60mm, 900x215x65mm,1000x250x65mm,140030050mm,or according to Clients' design
Variety	Cutted, Bent, Welded
Production Method	Cutting, welding, bending
Features	Toughness, light weight, High property of acid and alkali resistance, Bear high & low temperature, etc.
Applications	Electroplating industry, such as (1)Precious metal plating(Ag, Au, Rh, Pd) (2)Hard chrome plating(Cr6+) (3)Base metal plating(Cu, Zn, Ni) (4)Precious metal recovery, etc.
Packing	Plastic as inside, plywood case as outside, or according to client's demand

1. Titanium materials conductivity is poor. Usually, the current of the hook outside the solution is not more than 0.26A/CM². If the current is over the rated, the hook will be superheat leading to solution temperature rising, cooling capacity increasing, energy wasting, even damage the plastics tank. It could be improved with increasing the quantity of titanium basket or the cross-section size of the hook when the hook is superheat.

2. The hook and electrode are not allowed to be touch with flat or round, its easy make loose contact and leading to spot corrosion with this method.

3. Titanium basket mouth should be slightly higher than the solution level in order to prevent flowing out from the anode residue

4. Titanium basket bottom should be higher 100-150mm than parts which prevents burning out from the concentrated current of bottom parts

5. Titanium basket should be touch with the anode closely, or anode potential on the basket will rise sharply and cause chlorine evolution and OER leading to titanium damaged and additive oxidized

6. Titanium basket should be packed by titanium bags to protect the burr of plating coating. it is suggested to use double-bags method as the bags is used a long term and not be removed,

7. The anode bags (titanium bags) should be packed the titanium basket mouth tightly.

Bags bottom should be left a few inches space to store the possible anode mud.