STA High temperature MoSi2 Heating Element

The leading products of the company Molybdenum Disilicide Heating Element Type TC-1700 and TC-1800 elements are high-tech products researched and developed by experts from China and abroad.

MoSi2 heating element can quickly form a thin and adhesive anti-oxidizing layer of quartz glass (SiO2), under the high temperature oxidizing condition. If the protective layer was damaged, the element can reform a new one, so MoSi2 heating elements have a very good anti-oxidation properties, it also means that the heating element can be used on operation for a much longer time than the traditional one.

The resistivity of the Mosi2 heating element is not changing with the time, so a new one can be installed without effecting the old one. This can result of the huge saving in furnace maintenance fee sand time as well, increase the working efficiency. This is the key point of Mosi2 heating element being a better material and being widely used.

STA MoSi2 heating element is a resistance generate-heating component made from MoSi2 or the basic material. It is used in high temperature under the oxidizing atmosphere, it looks like glass in its surface and form a light SiO2 glass film which can protect the element not to be oxidized. So this kind of element has unique effect for resisting oxidization in the high temperature. It is used to the highest temperature up to 1800C during oxidizing atmosphere. According to your request, our company can produce the products of Pole, "U", "W" and "U"-right angle shapes, etc.

MoSi2 heating element can usually make use of furnace temperature from 1300C to 1800C. It is extensively used in the industries of metallurgy, glass, ceramic refractory, crystal electronic device, industrial furnace manufacture, etc.. It is an essential ideal element when the products are sintering in the high temperature.

Physics Characters

Volume Density	Bending Strength	Vickers Hardness	Porosity	Water absorption	Heating Elongation Rate
5.5 g/cm3	15-25 kg/cm3	(HV)570kg/mm2	7.4%	1.2%	4%

Order sample:

d=6mm, c=12mm, Le=200mm, Lu=180mm, a=30mm

Please specify as: dia6/12x200x180x30mm (dia d/cxLexLuxa mm)

d = the diameter of hot zone

c = the diameter of cold zone

Le = the length of hot zone

Lu = the length of cold zone