AAC PLANT (AUTOCLAVED AERATED CONCRETE)

1. SIMPLE INTRODUCE

Areated concrete brick (light brick ) is the light and porous buidling material. It has light keeping temperature cant burn and other advantages.it can be made into many kinds of bricks(for example:600×200×100,80×80×180,240×115×53,600×200×125),they could be used industry building and common building.they are more and more popular in the world.in the future,they will replace the Clay brick completely.

2.AUTOCLAVED AERATED CONCRETE COMMON CONCEPTION

Common concrete density is usually 1600-2400kg/m3,but Areated concrete are 500kg/m3,600kg/m3,700kg/m3.It has not the big grain,main use silicon material (for example:coal ash,sand,stone dust and others ),through making the material small for example sand,they can be used directly if has enough degree of small (for example coal ash.Mixing calcium material lime cement water to a special slop,then add the aluminum dust and the additive.Make the aluminum dust and the special slop have a Chemical reflect.then produce Hydrogen to make the concrete slop to expanding or swell,foam.Next,put them into the curing room to concreting cutting steaming curing,last,there will bacome the light brick,the porous rate is 70-80%.

3.DETAILED PRODUCT DESCRIPTION

foam block machine,

aerated autoclaved concrete plant, AAC block,aac production line,aac plant,AAC brick,autoclave aerated concrete block,concrete block machine,light weight block

1 Product weight is according to 600kg/m3 to control.

2 annual capacity 200,000M3.

3 set raw material proportion: cement 6.5%, raw lime 23%, flyash 68%, gypsum 3%, aluminum paste powder 350g/M3.

4 water and material rate 0.631

5 one mould product 2.88M3

6 Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.

7 casting slurry temperature 38-42 degree

8 body quiet stop. Time is 1.5-2.5housr, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa

9 Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.

10. Cement lime fly ash style aerated block raw material proportion

name	unit	Cement lime fly ash
flash	%	65-70
cement	%	6-15
lime	%	18-25
gypsum	%	3-5
Aluminum powder paste(600kg/m3)	1/10000	8
Water & material rate		0.60-0.65
Casting system	OC	36-40
Aluminum mixing time	S	30-40

11. Cement lime Sand style aerated block raw material proportion

Name	Unit	Cement Lime Sand
Sand	%	55-65
Cement	%	10-20
Lime	%	20-30
Gypsum	%	2-3
Aluminum powder paste(600kg/m3)	1/10000	8
Water & material rate		0.65-0.75
Casting system	OC	35-38
Aluminum mixing time	S	30-40