Reputable Brands Aac Plant (Aerated Autoclaved Concrete Block)

Raw material

fly ash,slag,lime,cinder, gangue,aluminum powder etc.

Fly ash style aerated block raw material proportion:

Parameter Name	Parameter Value
Fly ash	65-70%
cement	6-15%
lime	18-25%
gypsum	3-5%
Aluminum powder paste	8
Water & material rate	0.60-0.65
Casting temperature	36-40°C
Aluminum mixing time	30-40s

Sand style aerated block raw material proportion

Parameter Name	Parameter Value
Sand	55-65%
Cement	10-20%
Lime	20-30%
Gypsum	2-3%
Aluminum powder paste	8
Water & material rate	0.65-0.75
Casting temperature	35-38°C
Aluminum mixing time	30-40s

The advantage of aac block

aerated concrete block is a kind of new building material, and has theadvantages of environmental protection. Compared with the traditional claybrick,as follows;

1.light weight

Aerated concrete density is 400kg / m3 ~ 700kg / m3, equivalent to the 1 /3 of hollow clay brick, solid clay brick is 1 / 5, 1 / 4 concrete, lightweightaggregate concrete is lower than average density.

2.insulation resistance

Aerated concrete block internal contain great amount of bubbles and pores,and has good heat preservation performance.

3.durability

most of the aerated concrete block in natural carbonation,strength wasincreased slightly

4.resistance to water penetration

Aerated concrete block with closed independent globular structure, thusabsorbing moisture slowly.

5.easy of process

Aerated concrete block not only product a variety of specifications withinthe factory , can also be used for sawing, planing, drill, nail.

6.compressive strength

Aerated concrete compressive strength for 3.5MPa, 07 for 5.0MPa.

7.fire resistance

Aerated concrete block: low thermal conductivity, heat transfer is slow,can effectively resist fire, and to protect the structure from the effects offire.

8.sound absorption

Aeratedconcrete block has a spherical closed porous structure, and thus a certainsound absorption, sound absorption coefficient is 0.2 ~ 0.3.

The size of aac block

Length(mm)	Height(mm)	Width(mm)
600	200 250 300	60 120 180 240	75 100 125 150

Technological process

(1) all kinds of raw materials storage bin→ (2) measuring and batching → (3) mixing raw material with water → (4) prepared mould (5) → pouring → (6) vesicant and static curing → (7) demoulding → ( 8) rolling-over: horizontal cutting, vertical cutting → (9) be grouped into the autoclaved kettle → (10) high temperature and high pressure conservation → (11) out of autoclaved kettle for finished product → (12) testing finished product → (13)packaging → (14) stacking storage→(15) out of factory