8000 hours long service life molybdenum heaters mosi2 ceramic heating element

1.Molybdenum disilicide(MoSi₂) heating elementis a resistance generate-heating component made from MoSi₂or the basic material. It is used in high temperature under the oxidizing atmosphere, it looks like glass in its surface and form a light SiO₂glass film which can protect the element not to be oxidized. So this kind of element has unique effect for resisting oxidization in the high temperature. It is used to the highest temperature up to 1800°Cduring oxidizing atmosphere. And the applicable temperature is 500-1700°C.

2.Resistance property

The resistivity of element rapidly rises as the temperature rises. Under normal operating conditions, generally the element resistance doesn’t change with the service time changing. So the old and new elements can be mixed used.

3.Phiscal property

Volume Density	5.5g/cm3	Porosity	7.40%
Bending Strength	15-25kg/cm3	Water absorption	1.20%
Vickers Hardness	(HV)570kg/mm2	Heating Elongation Rate	4%

4.Chemistry property

MoSi₂heating element is used in the high temperature under oxidizing atmosphere. It will form the SiO₂film which can keep the element from being melted. When the temperature of element is more than 1700°C,the MoSi₂heating element must not be used in the temperature between 400°Cand 700°Cfor a long time; otherwise the element will be cremated under the strong oxidizing function in the low temperature.

5.The using temperature under the different atmosphere:

Atmosphere	The Maximum Using Temperature of Element
	1700 Grade	1800 Grade
NO2,CO2,O2,Air	1700°C	1800°C
He,Ar,Ne	1650°C	1750°C
SO2	1600°C	1700°C
CO,H2	1500°C	1600°C
WetH2	1400°C	1500°C
DryH2	1350°C	1450°C

6. Recommend Surface load

Furnace Temp (C )	1400	1500	1600	1650	1700
Surface load of hot zone(w/cm2)	<18	<15	<12	<10	<8

7.Usage

It can be used for high temperature furnace in ceramics, magnet, glass, metallurgy, refractory etc.

8. When you place order,pls kindly tell us the following things

Diameter of Hot Zone (D1):mm

Diameter of Cold End (D2):mm

Length of Hot Zone (Le):mm

Length of Cold End (Lu):mm

Shank spacing (A):mm

9. Installation of Elements

1) Vertically hanging

Under normal temperature, MoSi2 element is very brittleness, while under high temperature it is plasticity. So, the better way for installation if the U Shape element is to hang it vertically, to the furnace top through the support clamping chucks. The aim of such way is to avoid putting the mechanical stress directly to the element heat-generating end, or the element will easily be broken.

2) Support clamp

Support clamp are applied to 9/18 and 6/12 two kinds of elements respectively. The support clamp supports the whole weight of the element and the position of the element is also determined by it .therefore, it must be installed carefully to assure that the element it vertically hung. In order to prevent the element from being over heated locally, the taper part of the element lower end must put into the furnace chamber.

10.About our company

Our company have more than 20 years production experience, specialized in manufacturing high-temperature heating elements with strict quality control system, advanced equipment, strong technique power and complete test facilities. At present, our various products have passed ISO9001:2008 quality system authentication and have been exported to more than 40 countries and regions.